ABS 920 TORAY JAPAN

134

Form：Granules | Grade：Injection grade

Properties:

High mobilityHigh rigiditytransparent

Typical Applications:

small home appliancesCasterssporting goodsAutomotive sectorElectrical fieldElectronic field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative(4)

Product Description

Typical Applications:	small home appliances \| Casters \| sporting goods \| Automotive sector \| Electrical field \| Electronic field
Properties:	High mobility \| High rigidity \| transparent

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			透明性.超高刚性
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	20	%
tensile strength		ASTM D638/ISO 527	48	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	115
Tensile stress	23℃	ISO 527-2	54.0	Mpa
Elongation at Break	23℃	ASTM D-638	380	kg/cm
bending strength	23℃	ASTM D-790	780	kg/cm
Impact strength of cantilever beam gap	3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃	ASTM D-256	10；7；6	kg.cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃	ASTM D-256	9；7；6	kg.cm/cm
Bending stress	23℃	ASTM D-790	23500	kg/cm
Tensile strength at break	23℃	ASTM D-638	30	%
Tensile strength under yield	23℃	ASTM D-638	3.5	%
Rockwell hardness	23℃	ASTM D-785	115	R
bending strength		ASTM D790/ISO 178	74	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2160	kg/cm²(MPa)[Lb/in²]
tensile strength	23℃，Yield	ASTM D-638	490	kg/cm
Impact strength of cantilever beam gap		ASTM D256/ISO 179	108	kg·cm/cm(J/M)ft·lb/in
Tensile strain	23℃，Break	ISO 527-2	17	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8MPa，Unannealed	ISO 75-2/A	77.0	°C
Hot deformation temperature	Hot deformation temperature	18.56kg/cm	ASTM D-648	89	°C
Linear coefficient of thermal expansion		ASTM D-696	1.2×10	mm/mm/℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	83	℃（℉）
Combustibility (rate)		UL 94	HB
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃/10kg	ISO 1133	25	g/10min
Combustibility		UL -94	94HB
melt mass-flow rate	220℃ 10kg	ASTM D-1238	19-23	g/10min
Water absorption rate	浸入23℃水中24hr	ASTM D-570	0.3	%
density		ASTM D792/ISO 1183	1.09
Melt viscosity	220℃		3.5-5.0
melt mass-flow rate		ASTM D1238/ISO 1133	25	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.