SMA XIRAN® SG230

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.17 g/cm³
melt mass-flow rate		ISO1133	3.0 g/10min
SpiralFlow		内部方法	35.0 cm
Shrinkage rate		内部方法	0.61 %
Shrinkage rate	Shrinkage rate		内部方法	0.25 %
Water absorption rate		ASTMD570	0.20 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL94	HB

Mechanical properties	Test Condition	Test Method	Test Result
Bending stress		ISO178	120 MPa
Tensile modulus		ISO527-2	5300 MPa
Tensile stress	Break	ISO527-2	75.0 MPa
Tensile strain	Break	ISO527-2	2.5 %
Flexural modulus		ISO178	5400 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch		ISO179/1eU	32 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1eU	28 kJ/m²
Impact strength of cantilever beam gap		ISO180/A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/A	9.0 kJ/m²

Thermal performance	Test Method	Test Result
	ISO75-2/B	125 °C
		ISO75-2/A	120 °C
vicat	ISO306/B	122 °C
	ASTMD696	4.2E-05 cm/cm/°C
		ASTMD696	5.5E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.