Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Flow: | | mm/mm | 25.4E-3到134.6E-3 |
| Water absorption rate | | % | 0,15到0,53 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 122到125 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | Mpa | 27.03到260.0 |
| fracture | | % | 1,7到2,7 |
| fracture | | Mpa | 56.0到260.0 |
| fracture | | Mpa | 26.0到260.0 |
| fracture | | % | 2,0到4,6 |
| yield | | % | 1,5到5,0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 0.013到0.050 |
| Suspended wall beam without notch impact strength | | J/m | 0.085到0.462 |
| Charpy Notched Impact Strength | | kJ/m² | 0.789到3.762 |
| Impact strength of simply supported beam without notch | | kJ/m² | 7.892到21.357 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | V | 593到600 |
| dielectric strength | | V/mil | 490到610 |
| Surface Resistivity | | ohms | 1,0E+12到1,0E+14 |
| Volume resistivity | | ohms·cm | 1,0E+4到1,0E+16 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | °C | 220到265 |
| Linear thermal expansion coefficient | | mm/mm/°C | 30.5E-5到50.8E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare