PPA GV-6H EMS-CHEMIE SWITZERLAND

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityGlass fiber reinforcedaromatic

Typical Applications:

Electrical fieldElectronic fieldHome appliance componentsAutomotive interior partspowerTool productsHousehold goodssporting goodsEngineering accessoriesPneumatic applicationsConsumer goods sectorIndustrial applicationsAutomotive sectorHydraulic applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Home appliance components \| Automotive interior parts \| power \| Tool products \| Household goods \| sporting goods \| Engineering accessories \| Pneumatic applications \| Consumer goods sector \| Industrial applications \| Automotive sector \| Hydraulic applications
Properties:	Thermal stability \| Glass fiber reinforced \| aromatic

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
ISO Type		ISO 1874	PA66+PA6I/X. MH. 14-220. GF60
Flammability level		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2	2.0	%
tensile strength	Break	ISO 527-2	260	Mpa
Tensile modulus		ISO 527-2	22000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	9.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.5E-5	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Continuous use temperature	--4	Internal Method	220	°C
Continuous use temperature	Continuous use temperature	--3	ISO 2578	100 to 120	°C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	175	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	235	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.2	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	3.5	%
Shrinkage rate	Flow	ISO 294-4	0.10	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	33	KV/mm
Volume resistivity		IEC 60093	1.0E+14	ohms·cm
Surface resistivity		IEC 60093	--	ohms
Compared to the anti leakage trace index		IEC 60112		V
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	315	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.