Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.55 g/cm³ |
| Melt volume flow rate | | ISO1133 | 14.0 cm³/10min |
| Shrinkage rate | | ISO2577 | 0.90 % |
| Shrinkage rate | | ISO2577 | 0.30 % |
| Water absorption rate | | ISO62 | 0.20 % |
| Water absorption rate | | ISO62 | 0.40 % |
| | ISO1628 | 106.4 ml/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 220 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | 内部方法 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 10500 MPa |
| Tensile stress | Break | ISO527-2/5 | 155 MPa |
| Tensile strain | Break | ISO527-2/5 | 2.5 % |
| Flexural modulus | | ISO178 | 9000 MPa |
| Bending stress | | ISO178 | 220 MPa |
| Bending stress | | ISO178 | 210 MPa |
| Bending Strain | | ISO178 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 3.80 |
| CTI | | IEC60112 | 250 V |
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 28 kV/mm |
| | IEC60250 | 4.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 6E-05 cm/cm/°C |
| | ISO75-2/B | 220 °C |
| | ISO75-2/A | 205 °C |
| | ISO75-2/C | 125 °C |
| vicat | | ISO306/B50 | 225 °C |
| melting temperature | | ISO11357-3 | 220到255 °C |
| | ISO11359-2 | 3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.