| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| Shrinkage rate | | ISO 294-4 | 0.10 % |
| Water absorption rate | | ISO 62 | 3.5 % |
| Water absorption rate | | ISO 62 | 1.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO 2039-1 | 320 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10, -20 | HB |
| ISO Type | | ISO 1874 | PA66+PA6I/X, MH, 14-190, GF50 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 22500 Mpa |
| Tensile stress | | ISO 527-2 | 290 Mpa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 75 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1.0E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 33 KV/mm |
| CTI | | IEC 60112 | -- V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 250 °C |
| Heat distortion temperature | | ISO 75-2/C | 205 °C |
| Continuous use temperature | | ISO 2578 | 100 到 120 °C |
| Continuous use temperature | | 内部方法 | 220 °C |
| Melting temperature 5 | | ISO 11357-3 | 260 °C |
| | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| | ISO 11359-2 | 5.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.