HIPS POLYREX® PH-88 ZHENJIANG CHIMEI
628
- Properties:High impact resistanceheat-resisting
- Usages:Lighting fixturesHousehold goodsElectronic fieldElectrical field
- Certificates:SGSULMSDS
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 200°C/5.0kg | ISO1133 | 5.50 | cm3/10min |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 6.0 | g/10min |
| Shrinkage rate | ISO294-4 | 0.40到0.70 | % | |
| density | --3 | ASTMD792 | 1.05 | g/cm³ |
| 23°C | ISO1183 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 6.5 | kJ/m² |
| 23°C | ISO179 | 11 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 98 | J/m |
| 23°C,6.40mm | ASTMD256 | 83 | J/m | |
| -30°C | ISO180/1A | 6.0 | kJ/m² | |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| tensile strength | 屈服 | ISO527-2/50 | 26.0 | Mpa |
| 断裂4 | ASTMD638 | 23.5 | Mpa | |
| 断裂 | ISO527-2/50 | 24.0 | Mpa | |
| elongation | 断裂4 | ASTMD638 | 40 | % |
| 断裂 | ISO527-2/50 | 40 | % | |
| Rockwell hardness | L计秤 | ASTMD785 | 60 | |
| Bending modulus | --5 | ASTMD790 | 1930 | Mpa |
| --6 | ISO178 | 2100 | Mpa | |
| bending strength | --5 | ASTMD790 | 37.2 | Mpa |
| --6 | ISO178 | 37.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ASTMD15257 | 98.0 | °C |
| -- | ISO306/A50 | 96.0 | °C | |
| -- | ISO306/B50 | 90.0 | °C | |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 80.0 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 74.0 | °C | |
| 1.8MPa,退火 | ASTMD648 | 94.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 89.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4.0E-5到6.0E-5 | cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.