Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.20 g/cm³ |
| density | | | 3.0to5.0 Pa·s |
| Color | | | Amber |
| Color | | | Clear/Transparent |
| density | | | 0.998 g/cm³ |
| density | | | 1.0 hr |
| density | Pot Life | | 240 min |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 52 wk |
| Thermosetting components | | | 按重量计算的混合比:10 |
| Thermosetting components | | | 按重量计算的混合比:1.0 |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 88 |
| LapShearStrength | | | >13.8 MPa |
| relative permittivity | | | 3.34 |
| Volume resistivity | | | >1.0E+13 ohms·cm |
| Dissipation Factor | | | 4E-03 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | | 1.569 |
| transmissivity | | | >94.0 % |
| transmissivity | | | >98.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| operate temperature | | | -55-300 °C |
| operate temperature | | | 2.34 GPa |
| weight loss on heating | | | 0.060 % |
| weight loss on heating | | | 0.16 % |
| weight loss on heating | | | 0.49 % |
| DegradationTemperature | | TGA | 421 °C |
| Shear Strength | | | 23.4 MPa |
| operate temperature | | | -55-200 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >100 °C |
| Linear coefficient of thermal expansion | | | 4.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.9E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.