Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 2.0 % |
| Water absorption rate | | ISO 62 | 0.22 % |
| melt mass-flow rate | | ISO 1133 | 52 g/10min |
| Melt volume flow rate | | ISO 1133 | 45.0 cm3/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2900 Mpa |
| tensile strength | | ISO 527-2 | 64.0 Mpa |
| Tensile strain | | ISO 527-2 | 7.0 % |
| Nominal tensile fracture strain | | ISO 527-2 | 20 % |
| Flexural modulus | | ISO 178 | 2700 Mpa |
| bending strength | | ISO 178 | 91.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 100 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 3.90 |
| Dissipation Factor | | IEC 60250 | 2E-03 |
| Dissipation Factor | | IEC 60250 | 7E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 32 KV/mm |
| dielectric strength | | IEC 60243-1 | 19 KV/mm |
| relative permittivity | | IEC 60250 | 3.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 156 °C |
| Heat distortion temperature | | ISO 75-2/A | 100 °C |
| melting temperature | | ISO 11357-3 | 166 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.