'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPO 100Z ASAHI JAPAN
135
Form：Granules | Grade：Injection grade
Properties:
Chemical resistanceLow temperature resistanc
Typical Applications:
Fitness equipmentSports Equipment
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Fitness equipment | Sports Equipment |
| Properties: | Chemical resistance | Low temperature resistanc |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 16 | kJ/m² |
| machinability | Test Condition | Test Method | Test Result | Test Unit |
| Mold temperature | 40-70 | °C | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 | |
| 3.0mm | UL 94 | 5VA | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | ASTM D-570 | 0.10 | % | |
| Shrinkage rate | ASTM D-955 | 0.50-0.70 | % | |
| density | ASTM D-792 | 1.08 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | ASTM D790/ISO 178 | 59 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2250 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | R110 | ||
| tensile strength | ASTM D638/ISO 527 | 36 | kg/cm²(MPa)[Lb/in²] | |
| Elongation at Break | ASTM D638/ISO 527 | 40 | % | |
| UL flame retardant rating | UL 94 | V-0 | ||
| bending strength | ASTM D-790 | 59 | Mpa | |
| Bending modulus | ASTM D-790 | 2350 | Mpa | |
| Elongation at Break | ASTM D-638 | 40 | % | |
| tensile strength | ASTM D-638 | 39 | Mpa | |
| Yield,23°C | ISO 527-2 | 37.0 | Mpa | |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 30 | % |
| Bending modulus | 23°C | ISO 178 | 2370 | Mpa |
| bending strength | 23°C | ISO 178 | 66.0 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTM D648 | 85.0 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 78.0 | °C | |
| Linear coefficient of thermal expansion | MD：-30to65°C | ISO 11359-2 | 8E-05 | cm/cm/°C |
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 85 | ℃（℉） |
| Combustibility (rate) | UL 94 | V-0 | ||
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | ASTM D570/ISO 62 | 0.1 | % | |
| density | ASTM D792/ISO 1183 | 1.08 | ||
| Shrinkage rate | 2.00mm | Internal Method | 0.50-0.70 | % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | IEC 60250 | 4E-03 | |
| 100Hz | IEC 60250 | 3E-03 | ||
| Dielectric constant | 1MHz | IEC 60250 | 2.90 | |
| 100Hz | IEC 60250 | 2.90 | ||
| Dielectric strength | 2.00mm | IEC 60243-1 | 29 | KV/mm |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 | ohms·cm |
| Surface resistivity | IEC 60093 | 1E+16 | ohms |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.