PA/ABS N NM-19 BASF USA

Form：Granules | Grade：Injection grade

Properties:

UV resistanceEasy to processHigh mobilityHigh impact resistance

Typical Applications:

Automotive sectorAutomotive interior partssporting goodsLow temperature applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Automotive interior parts \| sporting goods \| Low temperature applications
Properties:	UV resistance \| Easy to process \| High mobility \| High impact resistance

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	1500	Mpa
bending strength		ISO 178	50.0	Mpa
Tensile modulus		ISO 527-2	1600	Mpa
tensile strength	Yield,23°C	ISO 527-2	35.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.4	%
tensile strength	Yield,23°C	ISO 527-2	43.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.5	%
Bending modulus		ISO 178	1800	Mpa
bending strength		ISO 178	62.0	Mpa
Tensile modulus		ISO 527-2	2000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	80.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	58.0	°C
Vicat softening temperature	--	ISO 306/A50	165	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	91.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04	cm/cm/°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	65.0	°C
Vicat softening temperature	--	ISO 306/A50	160	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	102	°C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	25.0	cm3/10min
Shrinkage rate		ISO 294-4	0.80	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.1	%
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	30.0	cm3/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	1MHz	IEC 60250	0.015
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	103
Ball Pressure Test		ISO 2039-1	86.0	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-3	>50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.