PA66 A3W BK BASF GERMANY

102

Form：Granules | Grade：Wear resistant grade

Properties:

Oil resistantFast forming cycleHigh mobilityheat-resisting

Typical Applications:

wheelEngine partsLaptop casebearing

Supplier(2)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	wheel \| Engine parts \| Laptop case \| bearing
Properties:	Oil resistant \| Fast forming cycle \| High mobility \| heat-resisting

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	3.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	4.6	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	48	J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	53	J/m
		Impact strength of cantilever beam gap	-40°C	ISO 180	4.0	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	4.5	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	6.0mm	UL 94	V-2
	UL flame retardant rating	3.0mm	UL 94	V-2
		UL flame retardant rating	1.5mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ISO 178	3100	Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.7	%
elongation	Yield,23°C	ASTM D638	4.5	%
tensile strength	Yield,23°C	ISO 527-2	88.0	Mpa
tensile strength	tensile strength	Yield,23°C	ASTM D638	85.0	Mpa
Tensile modulus	23°C	ISO 527-2	3300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Imp	3.0mm	UL 746	105	°C
RTI Imp	RTI Imp	6.0mm	UL 746	105	°C
RTI Str	0.75mm	UL 746	105	°C
RTI Imp	1.5mm	UL 746	105	°C
RTI Imp	RTI Imp	0.75mm	UL 746	105	°C
RTI Elec	6.0mm	UL 746	130	°C
	RTI Elec	3.0mm	UL 746	130	°C
		RTI Elec	1.5mm	UL 746	130	°C
		RTI Elec	RTI Elec	0.75mm	UL 746	130	°C
Melting temperature		ISO 3146	260	°C
RTI Str	6.0mm	UL 746	110	°C
	RTI Str	3.0mm	UL 746	110	°C
	RTI Str	RTI Str	1.5mm	UL 746	105	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	210	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0	°C
Melting temperature		ASTM D3418	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.14	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.8	%
	Water absorption rate	Equilibrium,50%RH	ASTM D570	2.8	%
		Water absorption rate	Saturation,23°C	ISO 62	8.5	%
		Water absorption rate	Water absorption rate	Saturation	ASTM D570	8.5	%
density		ISO 1183	1.14	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 A3W BK BASF GERMANY

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index