Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.30 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 20 g/10min |
| Shrinkage rate | | ASTM D955 | 1.2 % |
| Water absorption rate | | ASTM D570 | <0.20 % |
| Crystallinity | | | <30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 102 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 96 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3500 MPa |
| tensile strength | Break | ASTM D638 | 97.0 MPa |
| elongation | Break | ASTM D638 | >40 % |
| Flexural modulus | | ASTM D790 | 3500 MPa |
| bending strength | Yield | ASTM D790 | 159 MPa |
| compressive strength | | ASTM D695 | 131 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 3.30 |
| Dissipation Factor | | ASTM D150 | 4E-03 |
| Surface Resistivity | | ASTM D257 | 2E+16 ohms |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 18 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 160 °C |
| Glass Transition Temperature | | ASTM D3418 | 143 °C |
| melting temperature | | DSC | 339 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 4.7E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.