'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC EXL9134 7A8D006 SABIC INNOVATIVE NANSHA
81
Form：Granules | Grade：Injection grade
Properties:
High mobilityHigh ductility at low temShort molding cycle
Typical Applications:
Lighting applicationsElectronic and Electrical ApplicationsAerospace ApplicationsPlastic bag
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Lighting applications | Electronic and Electrical Applications | Aerospace Applications | Plastic bag |
| Properties: | High mobility | High ductility at low tem | Short molding cycle |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 | kJ/m² |
| -30°C | ISO 179/1eA | 35 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 67.0 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA | ||
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 825 | °C |
| 3.0 mm | IEC 60695-2-13 | 825 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | 50.0 mm Span4 | ASTM D790 | 2400 | Mpa |
| elongation | Break | ISO 527-2/50 | 110 | % |
| Break3 | ASTM D638 | 120 | % | |
| Yield | ISO 527-2/50 | 6.0 | % | |
| Yield3 | ASTM D638 | 6.0 | % | |
| tensile strength | Break | ISO 527-2/50 | 57.0 | Mpa |
| Break3 | ASTM D638 | 59.0 | Mpa | |
| Yield | ISO 527-2/50 | 56.0 | Mpa | |
| Yield3 | ASTM D638 | 58.0 | Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2000 | Mpa |
| --2 | ASTM D638 | 2100 | Mpa | |
| bending strength | Yield, 50.0 mm Span4 | ASTM D790 | 92.0 | Mpa |
| --5,6 | ISO 178 | 87.0 | Mpa | |
| Bending modulus | --5 | ISO 178 | 2100 | Mpa |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 120 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 to 60 | % | ||
| Temperature at the rear of the barrel | 270 to 295 | °C | ||
| Temperature in the middle of the barrel | 280 to 305 | °C | ||
| Temperature at the front of the material cylinder | 295 to 315 | °C | ||
| Spray nozzle temperature | 290 to 310 | °C | ||
| Processing (melt) temperature | 295 to 315 | °C | ||
| Mold temperature | 70 to 95 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 40 to 70 | rpm | ||
| Exhaust hole depth | 0.025 to 0.076 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 123 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9 | ISO 75-2/Af | 118 | °C | |
| Vicat softening temperature | -- | ASTM D152510 | 140 | °C |
| -- | ISO 306/B50 | 139 | °C | |
| -- | ISO 306/B120 | 141 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.1E-5 | cm/cm/°C |
| RTI | UL 746 | 120 | °C | |
| Linear coefficient of thermal expansion | Across Flow : -40 to 40°C | ASTM E831 | 6.2E-5 | cm/cm/°C |
| Across Flow : -40°C | ISO 11359-2 | 6.2E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 125 | °C | |
| RTI Imp | UL 746 | 115 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Outdoor applicability | UL 746C | f1 | ||
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % |
| Saturation, 23°C | ISO 62 | 0.40 | % | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.40 - 0.80 | % |
| Melt Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 15.0 | cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 16 | g/10 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.