PC 1803 COVESTRO BELGIUM

Form：Granules | Grade：Injection grade

Properties:

Flame retardantThermal stabilityenhanceHigh temperature resistanhigh viscosity

Typical Applications:

Automotive sectorLaptop caseElectrical fieldElectronic field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Laptop case \| Electrical field \| Electronic field
Properties:	Flame retardant \| Thermal stability \| enhance \| High temperature resistan \| high viscosity

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	1000μm	ISO 13468-2	89.0	%
Refractive index		ISO 489	1.573
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	25	%
Burning wire flammability index		IEC 60695-2-12	850	°C
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	108	Mpa
Bending modulus	23°C	ISO 178	2400	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
Tensile modulus	23°C	ISO 527-2/1	2400	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	72.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.8	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	174	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	159	°C
RTI Str		UL 746	150	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	150	°C
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B120	184	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	23°C	ISO 1183	1.15	g/cm³
melt mass-flow rate	330°C/2.16kg	ISO 1133	10	g/10min
Melt Volume Flow Rate (MVR)	330°C/2.16kg	ISO 1133	10.0	cm3/10min
Shrinkage rate	TD:2.00mm	ISO 294-4	0.85	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.85	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112		V
Dissipation factor	23°C,1MHz	IEC 60250	8E-03
Volume resistivity	23°C	IEC 60093	1E+17	ohms·cm
Dissipation factor	23°C,100Hz	IEC 60250	1E-03
Relative permittivity	23°C,1MHz	IEC 60250	2.80
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	2.90
Dielectric strength	23°C,1.00mm	IEC 60243-1	35	KV/mm
Surface resistivity		IEC 60093	1E+16	ohms
Compared to the anti leakage trace index	SolutionB	IEC 60112		V
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	121	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Electrolytic corrosion	23°C	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.