| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Demold Time | | 120to240 min |
| Thermosetting components | Resin | | 按重量计算的混合比:100按容量计算的混合比:100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:12按容量计算的混合比:13 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Viscosity | | | 0.25 Pa·s |
| Viscosity | | | 2.2 Pa·s |
| Viscosity | | | 2.8 Pa·s |
| Viscosity | | | 24 hr |
| Viscosity | | | 9.0to13 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 35to45 |
| tensile strength | | ASTM D638 | 11.9 MPa |
| elongation | Break | ASTM D638 | 190 % |
| tear strength | | ASTM D624 | 36.8 kN/m |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.06 g/cm³ |
| density | | | 1.10 g/cm³ |
| density | Base Resin | | 1.12 g/cm³ |
| Shrinkage rate | | ASTM D2566 | 0.020 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PeakExotherm | | | 49 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 103 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.