Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 6.00 cm3/10min |
| Melt volume flow rate | | ISO1133 | 9.00 cm3/10min |
| Shrinkage rate | | 内部方法 | 1.1到1.8 % |
| Shrinkage rate | | 内部方法 | 0.90到1.8 % |
| Water absorption rate | | ISO62 | 0.34 % |
| Water absorption rate | | ISO62 | 0.080 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 117 |
| | ISO2039-1 | 110 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 850 °C |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Limiting Oxygen Index | | ISO4589-2 | 21 % |
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap 4 | | ISO179/1eA | 5.5 kJ/m² |
| Simply supported beam without notch impact strength 5 | | ISO179/1eU | 无断裂 |
| Simply supported beam without notch impact strength 5 | | ISO179/1eU | 无断裂 |
| Suspended wall beam notch impact strength 6 | | ISO180/1A | 5.0 kJ/m² |
| Suspended wall beam notch impact strength 6 | | ISO180/1A | 6.0 kJ/m² |
| | ISO180/1U | 无断裂 |
| | ISO180/1U | 无断裂 |
| Impact strength of simply supported beam gap 4 | | ISO179/1eA | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2400 Mpa |
| Tensile stress | | ISO527-2/50 | 55.0 Mpa |
| Tensile stress | | ISO527-2/50 | 30.0 Mpa |
| Tensile strain | | ISO527-2/50 | 3.5 % |
| Tensile strain | | ISO527-2/50 | 100 % |
| Bending modulus 2 | | ISO178 | 2300 Mpa |
| Bending stress 3 | | ISO178 | 75.0 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 2.90 |
| | IEC60250 | 3.30 |
| | IEC60250 | 2.40 |
| Dissipation Factor | | IEC60250 | 3E-04 |
| Dissipation Factor | | IEC60250 | 3E-04 |
| Dissipation Factor | | IEC60250 | 2E-03 |
| Dissipation Factor | | IEC60250 | 0.020 |
| CTI | | IEC60112 | 600 V |
| CTI | | IEC60112 | 350 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 29 KV/mm |
| dielectric strength | | IEC60243-1 | 24 KV/mm |
| dielectric strength | | IEC60243-1 | 15 KV/mm |
| | IEC60250 | 2.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| BallPressure Test | | IEC60695-10-2 | Pass |
| | ISO11359-2 | 1.2E-04 cm/cm/°C |
| | ISO11359-2 | 1.3E-04 cm/cm/°C |
| 0.45MPa, Unanealed, 100mm span | | ISO75-2/Be | 120 °C |
| 1.8MPa, Unanealed, 100mm span | | ISO75-2/Ae | 55.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.