ABS

ABS XANTAR® C CP 200 Mitsubishi Chemical Corporation

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	23°C	ISO 180/4A	50 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	67.0 MPa
Nominal tensile fracture strain		ISO 527-2	>50 %
Tensile strain	Yield	ISO 527-2	4.5 %
tensile strength	Yield	ISO 527-2	45.0 MPa
Tensile modulus		ISO 527-2	2000 MPa
Bending modulus		ISO 178	1800 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
Vicat softening temperature		ISO 306/B50	112 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.10 g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.70 %
Shrinkage rate	MD	ISO 294-4	0.60 %
melt mass-flow rate	260°C/5.0kg	ISO 1133	26 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Surface resistivity		IEC 60093	>1.0E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.