Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 28 g/10min |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ISO 13468 | 87.0 % |
| Haze ratio | | ISO 14782 | 3.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 57.0 Mpa |
| Tensile strain | | ISO 527-2 | 13 % |
| Flexural modulus | | ISO 178 | 2630 Mpa |
| bending strength | | ISO 178 | 85.0 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.10 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 28 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | | 85.0to90.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 78.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.