Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.990 g/cm³ |
| Shrinkage rate | | ASTM D955 | 2.1 % |
| density | | ASTMD792 | 0.990 g/cm³ |
| Shrinkage rate | | ASTMD955 | 2.1 % |
| Shrinkage rate | | ASTMD955 | 1.3 % |
| Shrinkage rate | | | 1.3 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 65 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| OzoneResistance-Stress | | ASTMD518 | NoCracks |
| Ozone Resistance - Stressed | | ASTM D518 | No Cracks |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Abrasion | | ASTMD1630 | 110 mm³ |
| hardness | | ASTM D2240 | 65 |
| Abrasion | | ASTM D1630 | 110 mm³ |
| Tensile stress | | ASTM D412 | 2.10 MPa |
| Tensile stress | | | 3.00 |
| tensile strength | Break | ASTM D412 | 9.00 MPa |
| elongation | Break | ASTM D412 | 800 % |
| compression set | | ASTM D395 | 19 % |
| compression set | | | 46 |
| compression set | | | 69 |
| tear strength | | ASTM D624 | 30.0 kN/m |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| compression set | | ASTMD395 | 19 % |
| compression set | | ASTMD395 | 46 % |
| compression set | | ASTMD395 | 69 % |
| Tensile stress | | ASTMD412 | 2.10 MPa |
| Tensile stress | | ASTMD412 | 3.00 MPa |
| tensile strength | Break | ASTMD412 | 9.00 MPa |
| elongation | Break | ASTMD412 | 800 % |
| tear strength | | ASTMD624 | 30.0 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.