Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.20 % |
| Shrinkage rate | | | 0.58 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.24 % |
| spiral flow length | | ASTM D3123 | 4.50 cm |
| density | | | 1.55 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 30 |
| Shore hardness | | ASTM D2240 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| weight loss on heating | | 内部方法 | 580 °C |
| weight loss on heating | | 内部方法 | 570 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 13500 MPa |
| tensile strength | | ASTM D638 | 167 MPa |
| elongation | | ASTM D638 | 2.7 % |
| Flexural modulus | | ASTM D790 | 13600 MPa |
| bending strength | | ASTM D790 | 282 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 45 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 310 °C |
| Continuous use temperature | | UL 746B | 300 °C |
| Glass Transition Temperature | | ASTM D3418 | 152 °C |
| melting temperature | | ASTM D3418 | 372 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare