| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 10 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50-0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.50-0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 123 |
| Rockwell hardness | | ISO 2039-2 | 123 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Limiting Oxygen Index | | ASTMD2863 | 35 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 2400 Mpa |
| bending strength | | ASTM D790 | 93.8 Mpa |
| bending strength | | ISO 178 | 94.0 Mpa |
| Tensile modulus | | ASTM D638 | 2210 Mpa |
| Tensile modulus | | ISO 527-2/50 | 2200 Mpa |
| tensile strength | | ASTM D638 | 60.0 Mpa |
| tensile strength | | ISO 527-2/50 | 60.0 Mpa |
| tensile strength | | ASTM D638 | 57.9 Mpa |
| tensile strength | | ISO 527-2/50 | 58.0 Mpa |
| elongation | | ASTM D638 | 6.2 % |
| elongation | | ISO 527-2/50 | 6.0 % |
| elongation | | ASTM D638 | 110 % |
| elongation | | ISO 527-2/50 | 110 % |
| Flexural modulus | | ASTM D790 | 2400 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 58.8 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 139 °C |
| Heat distortion temperature | | ASTM D648 | 127 °C |
| Heat distortion temperature | | ISO 75-2/A | 125 °C |
| vicat | | ASTM D15256 | 149 °C |
| vicat | | ISO 306/A120 | 150 °C |
| vicat | | ISO 306/B50 | 144 °C |
| Ball pressure temperature | | IEC 60335-1 | >125 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 125 °C |
| RTI Imp | | UL 746 | 125 °C |
| RTI | | UL 746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.