PBT+PET Infino ASF-9810F LOTTE KOREA
0
- Properties:Fillermineral filler
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.6to1.9 % | |
| ISO 2577 | 1.6to1.9 % | ||
| ISO 2577 | 1.5to1.8 % | ||
| density | ASTM D792 | 1.31 g/cm³ | |
| ISO 1183 | 1.31 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 55 g/10min | |
| ISO 1133 | 55 g/10min | ||
| Shrinkage rate | ASTM D955 | 1.5to1.8 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 116 |
| R-Scale | ISO 2039-2 | 116 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.7 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 37 J/m | |
| ASTM D256 | 41 J/m | ||
| ISO 180/1A | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 58.8 MPa |
| Yield | ISO 527-2/50 | 58.0 MPa | |
| elongation | Break | ASTM D638 | 15 % |
| Tensile strain | Break | ISO 527-2/50 | 15 % |
| Flexural modulus | ASTM D790 | 2450 MPa | |
| ISO 178 | 2320 MPa | ||
| bending strength | ASTM D790 | 83.4 MPa | |
| ISO 178 | 80.0 MPa | ||
| Tensile modulus | ASTM D638 | 2500 MPa | |
| ISO 527-2/50 | 2350 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 60.0 °C | |
| vicat | ISO 306/B50 | 180 °C | |
| Heat distortion temperature | ASTM D648 | 165 °C | |
| ISO 75-2/B | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.