ABS 275 SINOPEC SHANGHAI GAOQIAO

261

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh gloss

Typical Applications:

Lighting fixturesElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(2)

Datasheet

Alternative Model(1)

Product Description

Typical Applications:	Lighting fixtures \| Electronic field \| Electrical field
Properties:	High impact resistance \| High gloss

Certificates

SGS

SGS

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			中冲通用级
Color			白色
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃,3.8kg	ASTM D-1238	2.6	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638/ISO 527	34	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	37	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	3	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	27	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	100	%
tensile strength	Yield,1/8",5mm/min	ASTM D-638	37	Mpa
tensile strength	tensile strength	1/8",5mm/min，Break	ASTM D-638	34	Mpa
elongation at yield	1/8",5mm/min	ASTM D-638	3	%
Elongation at Break	1/8",5mm/min	ASTM D-638	100	%
Impact strength of cantilever beam gap	23°C	ASTM D-256	27	KJ/m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525/ISO R306	107	℃（℉）
Vicat softening temperature	Vicat softening temperature	1/8",50℃/hr，120℃/10hr	ASTM D-1525	107	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	2.6	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	7.0-12.0	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.