Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 6.0 -- |
| Water absorption rate | | % | 2.0 -- |
| density | | g/cm³ | 1.40 -- |
| Shrinkage rate | | % | 0.60 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | MPa | 220 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 11000 6500 |
| tensile strength | Break | MPa | 225 130 |
| Tensile strain | Break | % | 3.0 6.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 20 25 |
| Impact strength of simply supported beam without notch | | kJ/m² | 85 90 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | kV/mm | 26 21 |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | 1E+14 1E+13 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | °C | 220 -- |
| Hot deformation temperature (HDT) | | °C | 160 -- |
| Continuous use temperature | | °C | 100to120 -- |
| Continuous use temperature | | °C | 180 -- |
| melting temperature | | °C | 260 -- |
| | cm/cm/°C | 2E-05 -- |
| | cm/cm/°C | 1E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare