Technical Data Sheet
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| | | 3.48 |
| Supporting hardness | | | 80 |
| LapShearStrength | | | 10.8 MPa |
| Volume resistivity | | | >7.0E+13 ohms·cm |
| Dissipation Factor | | | 7E-03 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| colour | | | Blue |
| density | | | 1.15 g/cm³ |
| | | 200到300 Pa·s |
| Curing Time | | | 1.0 hr |
| STORAGE STABILITY | | | 40000 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <20.0 µm |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 52 wk |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Operating | | | -55到175 °C |
| Operating | | | -55到275 °C |
| Operating | | | 3.02 GPa |
| DegradationTemperature | | | 344 °C |
| Shear Strength | | | 11.7 MPa |
| WeightLossonHeating | | | 0.27 % |
| WeightLossonHeating | | | 1.1 % |
| WeightLossonHeating | | | 3.0 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >65.0 °C |
| | | 4.1E-05 cm/cm/°C |
| | | 2.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.