PS Innova N 2380E VIDEOLAR BRAZIL

Usages:
packing
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	23 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	2.2 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break,23°C	ISO 527-2	55.0 MPa
elongation	Break,23°C	ASTM D638	2.3 %
elongation	elongation	Break,23°C	ISO 527-2	2.5 %
bending strength	23°C	ASTMD790	95.0 MPa
Tensile modulus	23°C	ASTMD638	3300 MPa
tensile strength	Break,23°C	ASTM D638	58.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	95.0 °C
Vicat softening temperature	--	ASTMD15253	107 °C
Vicat softening temperature	Vicat softening temperature	--	ASTMD15254	102 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTMD792	1.05 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTMD1238	1.5 g/10min
Shrinkage rate	MD	ASTM D955	0.30to0.60 %
Shrinkage rate	Shrinkage rate	--	ISO 294-4	0.30to0.60 %
Water absorption rate	Saturation	ASTM D570	<0.10 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	<0.10 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	80
Rockwell hardness	Rockwell hardness	M-Sale	ISO 2039-2	80

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.