Polyester, TS

Polyester, TS Keripol RW 1411 Hexion Inc.

Properties:
Filler glass fiber reinforced material inorganic filler
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	5.0 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	85.0 MPa
Bending modulus		ISO 178	16500 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	160 °C

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	2.10 g/cm³
Apparent density		ISO 60	1.00 g/cm³
Shrinkage rate		ISO 2577	0.10 %
Water absorption rate		ISO 62	15.0 mg
Shrinkage rate		ISO 2577	-0.030 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+12 ohms
Volume resistivity		IEC 60093	1E+13 ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	30 kV/mm
Relative permittivity	100Hz	IEC 60250	6.00
Dissipation factor	100Hz	IEC 60250	8E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0

Supplementary Information	Test Condition	Test Method	Test Result
Compression molding pressure			>10.0 MPa
Compression molding temperature			160to180 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.