PA6/6T Ultramid® TKR4340G6 LS BK
115
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| proportion | ISO 1183 | 1.46 g/cm³ | |
| Shrinkage rate | ISO 294 | 0.3 % | |
| ISO 294 | 0.7 % | ||
| Water absorption rate | ISO 62 | 4.8 % | |
| ISO 62 | 1.6 % | ||
| Smoke melt index | ISO 1133 | 45 cm3/10mir |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527 | 1100 Mpa | |
| tensile strength | ISO 527 | 150 Mpa | |
| elongation | ISO 527 | 2.5 % | |
| bending strength | ISO 178 | 240 Mpa | |
| Short mouth impact of simply supported beam | ISO 179 | 8 kJ/m² | |
| Simple supported beam without notch impact | ISO 179 | 65 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Fire rating 1.6mm | UL94 | V-0 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| IEC 60093 | 1E17 Ω.cm | ||
| dielectric constant | IEC 60250 | 0.015 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75 | 220 °C | ||
| melting temperature | ISO 11357 | 290 °C | |
| ISO 11359 | 2.3E-5 cm/cm/℃ | ||
| ISO 11359 | 7E-5 cm/cm/℃ | ||
| thermal conductivity | DIN 52612 | 0.37 W/(m.K) |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.