Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.20到0.30 % |
| water content | | ISO62 | 0.30 % |
| density | | ISO1183 | 1.42 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 800 MPa |
| Bending stress | | ISO178 | 160 MPa |
| Tensile stress | Break | ISO527-2 | 130 MPa |
| Tensile strain | Break | ISO527-2 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+14 ohms |
| dielectric strength | | ASTMD149 | 16 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO75-2/B | 155 °C |
| Heat Deflection Temperature | | ISO75-2/A | 143 °C |
| Linear thermal expansion coefficient | | ASTMD696 | 2.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.