Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO11443-A | 250 Pa·s |
| Water absorption rate | | ISO62 | 0.10 % |
| density | | ISO1183 | 1.38 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.30to0.50 % |
| Shrinkage rate | | ISO2577 | 0.15to0.35 % |
| Water absorption rate | | ISO62 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 12 kJ/m² |
| | ISO180 | 40 kJ/m² |
| | ISO180 | 40 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 11 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 10000 MPa |
| Tensile stress | | ISO527-2/5 | 135 MPa |
| Tensile strain | | ISO527-2/5 | 2.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+17 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 35 kV/mm |
| | IEC60250 | 3.60 |
| | IEC60250 | 3.40 |
| Dissipation Factor | | IEC60250 | 3E-03 |
| Dissipation Factor | | IEC60250 | 8.5E-03 |
| CTI | | IEC60112 | 175 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 134 °C |
| | ISO75-2/A | 126 °C |
| vicat | | ISO306/B50 | 132 °C |
| vicat | | ISO306/B120 | 134 °C |
| | ISO11359-2 | 2.5E-05 cm/cm/°C |
| | ISO11359-2 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.