Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.79 g/cm³ |
| Apparent density | | ASTM D1895 | 0.30 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.15to0.35 % |
| Water absorption rate | | ASTM D570 | 0.32 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 13800 MPa |
| bending strength | | ASTM D790 | 125 MPa |
| compressive strength | | ASTM D695 | 187 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 52 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 4.30 |
| Dissipation Factor | | ASTM D150 | 0.016 |
| arc resistance | | ASTM D495 | 133 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTME831 | 2.2E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648A | 260 °C |
| Heat distortion temperature | | ASTM D648A | >280 °C |
| thermal conductivity | | ASTMC518 | 0.31 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.