'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPA AS-4133HS SOLVAY USA
225
Form：Granules | Grade：Injection grade
Properties:
Aging resistanceHigh glossDimensional stabilityHigh rigidityHigh temperature strengthChemical resistanceFiller: Glass fiber reinfFiller by weight
Typical Applications:
Sports equipmentSpecial material for casting film
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Sports equipment | Special material for casting film |
| Properties: | Aging resistance | High gloss | Dimensional stability | High rigidity | High temperature strength | Chemical resistance | Filler: Glass fiber reinf | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178to19.964 | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | % | 23to25 | ||
| Burning wire flammability index | °C | 743to960 | ||
| Hot filament ignition temperature | °C | 721to926 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Fracture, 23 ℃ | 131.72to400.0 | MPa | ||
| Yield, 23 ℃ | 68.97to250.34 | MPa | ||
| Tensile modulus | 摩擦系数 | 0.15to0.52 | ||
| Fracture, 23 ℃ | % | 1.0to2.5 | ||
| % | 1.5to3.1 | |||
| Yield, 23 ℃ | % | 1.4to2.5 | ||
| compressive strength | 23℃ | 142.76to196.55 | MPa | |
| Poisson's ratio | 23℃ | 0.41 | ||
| Yield, 23 ℃ | 102.76to362.76 | MPa | ||
| shear strength | 23℃ | 88.28to107.59 | MPa | |
| Fracture, 23 ℃ | 108.28to262.76 | MPa | ||
| Yield, 23 ℃ | 12.62to270.34 | MPa | ||
| % | 1.5to2.6 | |||
| Fracture, 23 ℃ | 162.76to199.31 | MPa | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| 1.8MPa, unannealed | °C | 247to292 | ||
| 0.45MPa, annealed | °C | 296to320 | ||
| 0.45MPa, unannealed | °C | 275to308 | ||
| 8.0Mpa, unannealed | °C | 165to230 | ||
| flow | mm/mm/°C | 185.4E-5-25.4E-5 | ||
| 1.8MPa, unannealed | °C | 249to304 | ||
| flow | mm/mm/°C | 38.1E-5-50.8E-5 | ||
| RTI Elec | °C | 140to150 | ||
| RTI Imp | °C | 118to150 | ||
| Vicat softening temperature | °C | 258to313 | ||
| flow | mm/mm/°C | 195.6E-5-25.4E-5 | ||
| RTI | °C | 119to150 | ||
| Continuous use temperature | °C | 140to186 | ||
| transverse | mm/mm/°C | 68.6E-5-127.0E-5 | ||
| 1.8MPa, annealed | °C | 283to300 | ||
| transverse | mm/mm/°C | 63.5E-5-177.8E-5 | ||
| 0.45MPa, unannealed | °C | 273to312 | ||
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| 23℃,24hr | % | 0.30to0.51 | ||
| Balance, 23 ℃, 50% RH | % | 0.21to1.2 | ||
| Lateral flow: 23 ℃ | Across Flow, 23℃ | mm/mm | 119.4E-3-0.254 | |
| 23℃,24hr | % | 0.12to0.30 | ||
| Flow: 23 ℃ | Flow,23℃ | mm/mm | 48.3E-3-129.5E-3 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | 23℃ | 125 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.