Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.07 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 6.0 g/10min |
| Shrinkage rate | | ISO 294-4 | 0.80to1.2 % |
| Shrinkage rate | | ISO 294-4 | 0.80to1.2 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 31 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2000 MPa |
| tensile strength | | ISO 527-2/5 | 25.0 MPa |
| Tensile strain | | ISO 527-2/5 | 30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 3.5 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/B | 145 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 85.0 °C |
| vicat | | ISO 306/A120 | 155 °C |
| melting temperature | | | 160to165 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.