Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | <0.20 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| density | | ISO1183 | 1.80到2.00 g/cm³ |
| Apparent density | | ISO60 | 0.70到0.85 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.40到0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 850 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 875 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO527-2 | 5000到7000 MPa |
| Tensile stress | | ISO527-2 | 30.0到50.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 8000到10000 MPa |
| Bending stress | Compression Molded | ISO178 | 60.0到80.0 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 1.2到1.8 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 2.0到3.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 15到20 kV/mm |
| | IEC60250 | 4.005.00 |
| | IEC60250 | 4.005.00 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | >575 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 5.0E-5到6.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40到0.60 W/m/K |
| | ISO75-2/C | >200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.