PA66 A3X2G7 BASF GERMANY

Form：Granules | Grade：Flame retardant grade

Properties:

Electrical performanceFlame retardanthigh strengthHigh rigidityOil resistant

Typical Applications:

Electrical applicationsElectrical components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Electrical components
Properties:	Electrical performance \| Flame retardant \| high strength \| High rigidity \| Oil resistant

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	70	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ASTM D256/ISO 179	14/18	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	70/70	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	13/20	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	160/120	%
Tensile modulus		ASTM D638/ISO 527	9200	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	160/120	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	3/4	%
Elongation at Break		ASTM D638/ISO 527	3/4	%
Tensile modulus	23°C	ISO 527-2	11000	Mpa
tensile strength	Break,23°C	ISO 527-2	160	Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0	%
Bending modulus	23°C	ISO 178	9200	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	250	℃（℉）
Melting temperature			220	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.5-2/6-7	mm/mm.℃
	Linear coefficient of thermal expansion	MD		1.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		6.5E-05	cm/cm/°C
RTI Elec	0.40mm	UL 746	110	°C
	RTI Elec	0.75mm	UL 746	115	°C
		RTI Elec	1.5mm	UL 746	115	°C
		RTI Elec	RTI Elec	3.0mm	UL 746	115	°C
RTI Imp	0.40mm	UL 746	115	°C
	RTI Imp	0.75mm	UL 746	115	°C
		RTI Imp	1.5mm	UL 746	115	°C
		RTI Imp	RTI Imp	3.0mm	UL 746	115	°C
RTI Str	0.75mm	UL 746	130	°C
	RTI Str	1.5mm	UL 746	130	°C
	RTI Str	RTI Str	3.0mm	UL 746	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	25.0	cm3/10min
Shrinkage rate	TD	ISO 294-4	1.1	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.34	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257/IEC 60093	>1013/1010	Ω
Dielectric constant		ASTM D150/IEC 60250	3.6/5
Volume resistivity		ASTM D257/IEC 60093	1015/1012	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.