PA6 B3GF50 AKRO-PLASTIC GERMANY

Form：Granules | Grade：Wear resistant grade

Properties:

Filler: Glass fiber reinf50% filler by weight

Typical Applications:

engineering application

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	engineering application
Properties:	Filler: Glass fiber reinf \| 50% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.6mm	IEC 60695-2-12	650	°C
UL flame retardant rating	1.6mm	UL 94	HB
Burning rate	1.00mm	FMVSS302	<100	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	340	Mpa
Bending modulus		ISO 178	14900	Mpa
Tensile strain	Break	ISO 527-2/5	2.5	%
tensile strength	Break	ISO 527-2/5	240	Mpa
Tensile modulus		ISO 527-2/1	17000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	220	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220	°C
TemperatureIndex	50%LossofTensileStrength,5000hr	IEC 216	160to175	°C
TemperatureIndex	TemperatureIndex	50%LossofTensileStrength,20000hr	IEC 216	130to150	°C
Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	9.4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	1.1E-05	cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	185	°C
Melting temperature		DIN EN11357-1	220	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Hygroscopicity	70°C，62%RH	ISO 1110	1.3to1.6	%
Water absorption rate	Saturation,23°C	ISO 62	4.5to5.1	%
Shrinkage rate	MD	ISO 294-4	0.20	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.90	%
Spiral flow length		Internal Method	43.0	CM
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Volume resistivity		IEC 60093	1E+13	ohms·cm
Surface resistivity		IEC 60093	1E+12	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H961/30	ISO 2039-1	270	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ReinforcementContent		ISO 1172	50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.