Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | ASTM D955 | 1.2 % |
Water absorption rate | | ASTM D570 | 0.048 % |
density | | ASTM D792 | 1.62 g/cm³ |
Shrinkage rate | | ASTM D955 | 0.39 % |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
Light reflectance | | ASTME1331 | >96 % |
Light reflectance | | ASTME1331 | >95 % |
Light reflectance | | ASTME1331 | >95 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 6730 MPa |
tensile strength | | ISO 527-2 | 73.3 MPa |
Tensile strain | Break | ISO 527-2 | 1.5 % |
Flexural modulus | | ISO 178 | 6230 MPa |
bending strength | | ISO 178 | 108 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/1A | 2.4 kJ/m² |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ASTME831 | 5.8E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 1E-04 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 1.2E-04 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 1.4E-04 cm/cm/°C |
melting temperature | | ISO 11357-3 | 289 °C |
Linear coefficient of thermal expansion | | ASTME831 | 2.9E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 1.7E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 2E-05 cm/cm/°C |
Heat distortion temperature | | ISO 75-2/B | 269 °C |
Heat distortion temperature | | ISO 75-2/A | 214 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.