Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 2.7to4.9 g/10min |
| Melt volume flow rate | | ISO 1133 | 2.50to4.50 cm3/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 32 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 82.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| FailureEnergy-DynaTest | | DIN 53373 | 240 J/cm |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-3 | 44.0 Mpa |
| elongation | | ISO 527-3 | 560 % |
| elongation | | ISO 527-3 | 710 % |
| OTr | | ASTM D3985 | 1200 cm³/m²/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 140 g/m²/24hr |
| film thickness | | | 50 µm |
| tensile strength | | ISO 527-3 | 36.0 Mpa |
| tensile strength | | ISO 527-3 | 45.0 Mpa |
| tensile strength | | ISO 527-3 | 35.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A50 | 91.0 °C |
| melting temperature | | DSC | 110to120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.