| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.70 % |
| Water absorption rate | | ISO62 | 0.30 % |
| density | | ISO1183 | 1.15 g/cm³ |
| Melt volume flow rate | | ISO1133 | 6.50 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 37 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| TearStrength- | | ISO34 | 265 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 65.0 MPa |
| Tensile stress | | ISO527-2 | 32.0 MPa |
| Tensile stress | Break | ISO527-2 | 21.0 MPa |
| Tensile stress | | ISO527-2 | 3.50 MPa |
| Tensile stress | | ISO527-2 | 3.40 MPa |
| Tensile stress | | ISO527-2 | 5.70 MPa |
| Tensile stress | | ISO527-2 | 2.60 MPa |
| Tensile stress | | ISO527-2 | 11.2 MPa |
| Tensile stress | | ISO527-2 | 8.70 MPa |
| Tensile stress | | ISO527-2 | 9.30 MPa |
| Tensile stress | | ISO527-2 | 14.0 MPa |
| Tensile strain | Break | ISO527-2 | 960 % |
| NominalTensileStrainatBreak | | ISO527-2 | 280 % |
| Tensile stress | | ISO527-2 | 5.40 MPa |
| Tensile stress | | ISO527-2 | 6.00 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357-3 | 214 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.