PBT HX3091HP SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedHigh impact resistance

Typical Applications:

Automotive ApplicationsElectrical applications

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical applications
Properties:	Glass fiber reinforced \| High impact resistance

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity		Internal Method	400000	mPa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	35.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--1	ASTM D638	2530	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2500	Mpa
tensile strength	Yield2	ASTM D638	56.0	Mpa
	tensile strength	Yield	ISO 527-2/50	46.0	Mpa
		tensile strength	Break2	ASTM D638	30.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	45.0	Mpa
elongation	Yield2	ASTM D638	3.6	%
	elongation	Yield	ISO 527-2/50	3.0	%
		elongation	Break2	ASTM D638	300	%
		elongation	elongation	Break	ISO 527-2/50	60	%
Bending modulus	50.0 mm Span3	ASTM D790	2400	Mpa
Bending modulus	Bending modulus	--4	ISO 178	2150	Mpa
bending strength	--4,5	ISO 178	77.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span3	ASTM D790	77.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	112	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	49.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	50.0	°C
Vicat softening temperature	--	ASTM D152512	170	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	171	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.0E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	250°C/2.16 kg	ASTM D1238	21	g/10 min
Melt Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	19.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	1.8 - 2.2	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	1.8 - 2.2	%
Water absorption rate	Saturation, 23°C	ISO 62	0.34	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.080	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PBT HX3091HP SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index