Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 | % |
| Shrinkage rate | 流量 | ISO 294-4 | 1.3 | % |
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 3.0 | % |
| Water absorption rate | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.3 | % |
| Stickiness number | 96% H2SO4 | ISO 307 | 95.0 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 114 | |
| Tensile modulus | | ISO 527-2 | 2400 | Mpa |
| tensile strength | 屈服 | ISO 527-2 | 62.0 | Mpa |
| elongation | 屈服 | ISO 527-2 | 4.5 | % |
| Nominal tensile fracture strain | | ISO 527-2 | 17 | % |
| Bending modulus | | ISO 178 | 2100 | Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 135 | °C |
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 62.0 | °C |
| vicat softening point | | ISO 306/B50 | 181 | °C |
| Melting temperature | | ISO 11357-3 | 218 | °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.1E-4 | cm/cm/°C |
| Linear coefficient of thermal expansion | 流动 : -40 到 23°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 流动 : 55 到 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1.2E-4 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : -40 到 23°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 55 到 160°C | ISO 11359-2 | 1.8E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC 62631-3-1 | 1.0E+13 | ohms·m |
| Dielectric strength | | IEC 60243-1 | 30 | KV/mm |
| Relative permittivity | 1 MHz | IEC 62631-2-1 | 3.20 | |
| Relative permittivity | 100 Hz | IEC 62631-2-1 | 3.60 | |
| Dissipation factor | 100 Hz | IEC 62631-2-1 | 0.014 | |
| Dissipation factor | 1 MHz | IEC 62631-2-1 | 0.016 | |
| Leakage Trace Index | | IEC 60112 | 600 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt density | | | 0.900 | g/cm³ |
| Specific Heat Capacity of Melt | | | 2750 | J/kg/°C |
| Thermal Conductivity of Melt | | | 0.18 | W/m/K |
| Emission of Organic Compounds | | VDA 277 | 3.10 | µgC/g |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying time - hot air dryer | | | 2.0 到 4.0 | hr |
| Suggested maximum moisture content | | | 0.15 | % |
| Processing (melt) temperature | | | 230 到 290 | °C |
| Melt Temperature, Optimum | | | 250 | °C |
| Mold temperature | | | 50 到 90 | °C |
| Mold Temperature, Optimum | | | 70 | °C |
| Maintain pressure | | | 50.0 到 100 | Mpa |
| Maintain pressure | Drying Recommended | | yes | |
| Hold Pressure Time | | | 4.00 | s/mm |
| squeeze | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 80 | °C |
| drying time | | | 3.0 到 4.0 | hr |
| Suggested maximum moisture content | | | 0.060 | % |
| Melt Temperature | | | 235 到 250 | °C |
| Extrusion Melt Temperature, Optimum | | | 240 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ISO 4589-2 | 27 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.