PPO GFN1-845 SABIC INNOVATIVE US

127

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanHydrolysis resistance

Typical Applications:

Automotive componentsLaptop case

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Laptop case
Properties:	High temperature resistan \| Hydrolysis resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	21.7	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	28	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	25	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	11	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	9.4	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	33	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ISO 527-2	64.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	63.0	Mpa
Tensile modulus		ISO 527-2/1	4400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	4350	Mpa
elongation	Break	ASTM D638	3.0	%
Tensile strain	Break	ISO 527-2	3.0	%
Bending modulus	50.0mmSpan4	ASTM D790	3840	Mpa
	Bending modulus	100mmSpan5	ASTM D790	3590	Mpa
	Bending modulus	Bending modulus		ISO 178	4160	Mpa
bending strength		ISO 178	122	Mpa
	bending strength	Yield,50.0mmSpan4	ASTM D790	116	Mpa
	bending strength	bending strength	Yield,100mmSpan5	ASTM D790	108	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI Elec		UL 746	90.0	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	131	°C
	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	132	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	122	°C
			Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	125	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	124	°C
Vicat softening temperature	--	ISO 306/B50	131	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	134	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	5.1E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.1E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f1
Water absorption rate	24hr	ASTM D570	0.060	%
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.50	%
Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	16.4	cm3/10min
melt mass-flow rate	300°C/5.0kg	ASTM D1238	17	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition	HWI	UL 746	PLC 5
High voltage arc tracing rate	HVTR	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 4
Arc resistance		ASTM D495	PLC7
Dissipation factor	1MHz	ASTM D150	1.4E-03
Dielectric constant	1MHz	ASTM D150	2.90
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L-Sale	ASTM D785	104

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPO GFN1-845 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index