Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 30 g/10min |
| Melt volume flow rate | | ISO 1133 | 31.4 cm3/10min |
| Shrinkage rate | | ASTM D955 | 0.40-0.60 % |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 良流动 |
| purpose | | | 杂货 文具 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2/5 | 64.1 Mpa |
| Flexural modulus | | ISO 178 | 3700 Mpa |
| bending strength | | ISO 178 | 123 Mpa |
| Flexural modulus | | ASTM D790/ISO 178 | 3330(MPa) kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 97(MPa) kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.08 kg·cm/cm(J/M)ft·lb/in |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 30 g/10min |
| Water absorption rate | | ASTM D570/ISO 62 | 0.2 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 86.8 °C |
| vicat | | ISO 306/B | 102 °C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
| ball-indentation hardness | | EMAC | 95 °C |
| Combustibility (rate) | | UL 94 | HB |
| Heat distortion temperature | | ASTM D648/ISO 75 | 90 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 109 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.