ABS M203FC 000000 ELIX POLYMERS SPANISH

Form：Granules | Grade：Medical grade

Properties:

High mobility

Typical Applications:

medical careShell

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	medical care \| Shell
Properties:	High mobility

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Burning rate		ISO 3795	60	mm/min
Injection speed		ISO 294	240	mm/sec
Melting temperature		ISO 294	240	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	15	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Bending modulus	23°C	ISO 178	2400	Mpa
bending strength	23°C	ISO 178	70	Mpa
Tensile modulus	23°C	ISO 527-2	2400	Mpa
Elongation at Break	23°C	ISO 527-2	>=15	%
Elongation at Break	Elongation at Break	Yield，23°C	ISO 527-2	2.6	%
tensile strength	Yield，23°C	ISO 527-2	46	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	94	°C
Vicat softening temperature	5.10kg	ISO 306/A50	99	°C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	98	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃/10.0Kg	ISO 1133	31	g/10min
melt mass-flow rate	melt mass-flow rate	线性收缩率	ISO 294-4	0.4-0.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	相对漏电起痕指数	IEC 60112	600	V
	Dissipation factor		IEC 60250	0.09
	Dissipation factor	Dissipation factor		IEC 60250	0.05
Dielectric constant		IEC 60250	3	100HZ
Dielectric constant	Dielectric constant		IEC 60250	2.9	1MHz
Volume resistivity		IEC 60093	1E+13	Ω.cm
Surface resistivity		IEC 60093	1E+15	Ω.cm
Dielectric strength	1.00mm	IEC 60243-1	35	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	110	Mpa
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
Ignition temperature of heating wire	2.00mm	IEC 60695-2-12	700	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.