PA66 Vydyne® 75HF

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.14 g/cm³
Water absorption rate		ISO 62	8.5 %
Water absorption rate	Water absorption rate		ISO 62	2.5 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527-2	50.0 MPa
Tensile strain		ISO 527-2	5.0 %
Nominal tensile fracture strain		ISO 527-2	>200 %
Flexural modulus		ISO 178	2200 MPa
bending strength		ISO 178	70.0 MPa
Poisson's ratio		ISO 527-2	0.40
Tensile modulus		ISO 527-2	2700 MPa
tensile strength		ISO 527-2	80.0 MPa
	tensile strength		ASTM D882	105 MPa
	tensile strength	tensile strength		ASTM D882	123 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap		ISO 180	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	4.0 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	4.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak

film	Test Condition	Test Method	Test Result
Secant modulus		ASTM D882	392 MPa
Secant modulus	Secant modulus		ASTM D882	444 MPa
tensile strength		ASTM D882	121 MPa
Tensile strain		ASTM D882	7.0 %
Tensile strain	Tensile strain		ASTM D882	6.7 %
tensile strength		ASTM D882	105 MPa
Tensile strain		ASTM D882	500 %
Dart impact		ASTM D1709	>2100 g
Elmendorf tear strength		ASTM D1922	100 g
Elmendorf tear strength	Elmendorf tear strength		ASTM D1922	110 g
elongation		ASTM D882	450 %

Thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature (HDT)		ISO 75-2/B	125 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/A	45.0 °C
melting temperature		ISO 11357-3	220 °C
		ISO 11359-2	1E-04 cm/cm/°C
			ISO 11359-2	1E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.