Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.52 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 10.0 cm³/10min |
| Shrinkage rate | | DIN 16901 | 0.80to1.5 % |
| Water absorption rate | | | <0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 6500 MPa |
| bending strength | | ISO 178 | 150 MPa |
| Bending Strain | | ISO 178 | 3.9 % |
| Tensile modulus | | ISO 527-2 | 7500 MPa |
| tensile strength | Break | ISO 527-2 | 105 MPa |
| Tensile strain | Yield | ISO 527-2 | 2.9 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 42 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| insulation resistance | | IEC 60167 | >1.0E+12 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | DIN 52612 | 0.40 W/m/K |
| Heat distortion temperature | | ISO 75-2/A | 315 °C |
| Continuous use temperature | | UL 746B | 250 °C |
| maximum service temperature | | | 260 °C |
| Linear coefficient of thermal expansion | | DIN 53752 | 3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.