Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | ASTM D955 | 0.39to0.61 % |
Shrinkage rate | | ISO 294-4 | 0.28to1.3 % |
Water absorption rate | | ISO 62 | 6.5to7.1 % |
Water absorption rate | | ISO 62 | 2.0to2.3 % |
density | | ASTM D792 | 1.34to1.36 g/cm³ |
density | | ISO 1183 | 1.34to1.37 g/cm³ |
hardness | Test Condition | Test Method | Test Result |
---|
ball-indentation hardness | | ISO 2039-1 | 185 MPa |
flammability | Test Condition | Test Method | Test Result |
---|
Burning wire flammability index | | IEC 60695-2-12 | 650to960 °C |
Limiting Oxygen Index | | ISO 4589-2 | 23to24 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179 | 3.0to12 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179 | 34to46 kJ/m² |
Impact strength of cantilever beam gap | | ASTM D256 | 37to61 J/m |
Impact strength of cantilever beam gap | | ISO 180 | 4.0to10 kJ/m² |
Suspended wall beam without notch impact strength | | ISO 180 | 30to36 kJ/m² |
Multi axis Instrumented Impact Energy | | ISO 6603-2 | 2.00to3.63 J |
Multi axis Instrumented Peak Impact Force | | ISO 6603-2 | 700to813 N |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
bending strength | | ASTM D790 | 130to200 MPa |
bending strength | | ISO 178 | 144to186 MPa |
Tensile modulus | | ASTM D638 | 6110to6210 MPa |
Tensile modulus | | ISO 527-2 | 4700to8890 MPa |
tensile strength | | ASTM D638 | 116to125 MPa |
tensile strength | | ISO 527-2 | 92.6to125 MPa |
elongation | | ASTM D638 | 2.0to4.0 % |
elongation | | ISO 527-2 | 2.4to5.0 % |
Flexural modulus | | ASTM D790 | 4770to5810 MPa |
Flexural modulus | | ISO 178 | 4690to5870 MPa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
Surface Resistivity | | IEC 60093 | 1.0E+10到2.5E+14 ohms |
Volume resistivity | | IEC 60093 | 1.0E+13到2.5E+15 ohms·cm |
dielectric strength | | IEC 60243-1 | 11to37 kV/mm |
relative permittivity | | IEC 60250 | 4.25 |
Dissipation Factor | | IEC 60250 | 0.013to0.027 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTMD648 | 200to216 °C |
vicat | | ISO 306 | 199to211 °C |
melting temperature | | ISO 11357-3 | 222 °C |
melting temperature | | ISO 3146 | 220 °C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 3.0E-5到3.8E-5 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-05 cm/cm/°C |
Heat distortion temperature | | ASTM D648 | 180to204 °C |
Heat distortion temperature | | ISO 75-2/A | 189to192 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.