Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 5.5 % |
| Water absorption rate | | ISO 62 | 1.8 % |
| density | | ASTM D792 | 1.32 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3500 MPa |
| tensile strength | Yield | ASTM D638 | 70.0 MPa |
| elongation | Break | ASTM D638 | 20 % |
| Flexural modulus | | ASTM D790 | 3000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 180 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.