'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA6 73G30L NC010 DUPONT USA
372
Form：Granules | Grade：Injection grade
Properties:
High temperature resistanenhance
Typical Applications:
Electronic appliancesWear resistant accessoriesHome appliance accessories
Product Description
Certificates(1)
Datasheet
Alternative(3)
Product Description
| Typical Applications: | Electronic appliances | Wear resistant accessories | Home appliance accessories |
| Properties: | High temperature resistan | enhance |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 100 | kJ/m² |
| -30°C | ISO 180/1U | 90 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 | kJ/m² |
| -30°C | ISO 179/1eU | 80 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Atomization | G-value(condensate) | ISO 6452 | 1E-04 | g |
| F-value(refraction) | ISO 6452 | 95 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Extreme Oxygen Index | ISO 4589-2 | 21 | % | |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | ||
| 3.0mm | UL 94 | HB | ||
| 1.5mm | UL 94 | HB | ||
| Burning rate | 1.00mm | ISO 3795 | 25 | mm/min |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ISO 527-2 | 10000 | Mpa | |
| tensile strength | Break | ISO 527-2 | 180 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.5 | % |
| Tensile creep modulus | 1hr | ISO 899-1 | -- | Mpa |
| 1000hr | ISO 899-1 | -- | Mpa | |
| Bending modulus | ISO 178 | 8500 | Mpa | |
| bending strength | ISO 178 | 240 | Mpa | |
| Compressive stress | ISO 604 | 160 | Mpa | |
| shear strength | ASTM D732 | 60.0 | Mpa | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ASTM D638/ISO 527 | 9100 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 9000 | kg/cm²(MPa)[Lb/in²] | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1E-04 | cm/cm/°C |
| MD | ISO 11359-2 | 1.4E-05 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 221 | °C | |
| Glass transition temperature | ISO 11357-2 | 60.0 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 210 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 220 | °C | |
| HDT | ASTM D648/ISO 75 | 221 | ℃（℉） | |
| HDT | ASTM D648/ISO 75 | 210 | ℃（℉） | |
| Melting temperature | 221 | ℃（℉） | ||
| Vicat softening temperature | ASTM D1525/ISO R306 | 215 | ℃（℉） | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | TD | ISO 294-4 | 0.60 | % |
| MD | ISO 294-4 | 0.20 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 6.3 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 1.9 | % | |
| ASTM D570/ISO 62 | 1.8 | % | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | ||
| CTI | UL 746 | PLC 0 | ||
| Dissipation factor | 100Hz | IEC 60250 | 0.022 | |
| Relative permittivity | 100Hz | IEC 60250 | 3.80 | |
| Volume resistivity | IEC 60093 | 1E+14 | ohms·cm | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| EmissionofOrganicCompounds | VDA277 | 8.50 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.